Property |
Unit |
313 |
4302 |
4302-4 |
8302 |
8306 |
Type |
|
Si condensation |
Si addition |
|
PU |
PU |
Color |
|
B/W/G |
B/W/G |
B/W/G |
Colorless or light yellow transparent |
Light-yellow |
Mix ratio |
By weight |
6:1 |
1:1 |
1:1 |
1:1 |
5:1 |
Viscosity |
mPa·s |
3000±500 |
4000±500 |
4000±500 |
1000±100 |
7000±1000 |
Specific gravity |
g/cm3 |
1.6±0.1 |
1.6±0.1 |
1.8±0.1 |
1.1±0.1 |
1.5±0.1 |
Working time |
min |
30~40 |
30~60 |
30~60 |
40~60 |
20~40 |
Curing time |
h |
3 |
4 |
4 |
1.5 |
4 |
Hardness |
JIS A |
50±5 |
50±5 |
50±5 |
50±5 |
50±5 |
Thermal conductivity |
W/m·k |
0.8 |
0.6~0.8 |
1.0 |
0.2 |
0.8 |
Volume resistance |
Ω·cm |
>1E+15 |
>1E+14 |
>1E+14 |
>1E+14 |
>1E+14 |
Flame class |
UL |
HB |
V-0 |
V-0 |
V-0 |
V-0 |
Property |
Unit |
2386 |
2391 |
2491 |
2496 |
3694 |
7191 |
Color |
|
W/B/G |
W/B/G |
W/B/G |
W/B/G |
W/B/G |
B |
Appearance |
|
Paste |
Paste |
Paste |
Paste |
Medium-paste |
Flowable |
Specific gravity |
g/cm3 |
1.35 |
1.46 |
1.40 |
1.38 |
1.35 |
1.4 |
Tack-free time |
min |
5~20 |
5~10 |
5~10 |
9~20 |
5~20 |
15~30 |
Hardness |
JIS A |
50 |
42 |
44 |
45 |
54 |
30 |
Tensile strength |
Mpa |
1.2 |
2.0 |
2.0 |
2.3 |
2.0 |
1.2 |
Elongation at break |
% |
≥120 |
≥250 |
≥200 |
≥300 |
≥200 |
≥200 |
Shear strength |
Mpa |
1.2 |
1.8 |
1.8 |
2.2 |
1.5 |
1.5 |
Volume resistance |
Ω·cm |
≥1.0E+15 |
≥0.5E+15 |
≥1.0E+15 |
≥0.5E+15 |
≥1.0E+15 |
≥0.5E+15 |
Notes |
Cure condition: 25℃, RH75%; 7191 is a two-component adhesive, the entire cure time is 2h |
Property |
Unit |
3323 |
3901R |
4326 |
Color |
|
W/B/G |
R |
R |
Appearance |
|
Paste |
Flowable |
Medium-paste |
Specific gravity |
g/cm3 |
1.0~1.1 |
1.25~1.35 |
1.4~1.5 |
Tack-free time |
min |
5~35 |
10~30 |
5~10 |
Hardness |
JIS A |
20~35 |
25~45 |
35~50 |
Tensile strength |
Mpa |
>1.0 |
>1.0 |
>2.9 |
Elongation at break |
% |
≥100 |
150~350 |
≥160 |
Volume resistance |
Ω·cm |
≥1.0E+15 |
≥0.5E+15 |
≥0.34E+15 |
Property |
unit |
2740 |
2741 |
2742 |
2743 |
Color |
|
White |
White |
White |
White |
Appearance |
|
Paste |
Paste |
Paste |
Flowable |
Specific gravity |
g/cm3 |
1.7 |
2.5 |
2.7 |
2.9 |
Tack-free time |
min |
3~6 |
2~6 |
2~5 |
5~20 |
Entirety cure time |
h |
24(2mm) |
24(2mm) |
24(2mm) |
24(2mm) |
Hardness |
JIS A |
60 |
65 |
70 |
93 |
Thermal conductivity |
W/m·k |
0.8 |
1.2 |
2.0 |
3.0 |
Volume resistance |
Ω·cm |
1.0*1015 |
1.0*1015 |
1.0*1015 |
7.4*1014 |
Shear strength |
Mpa |
>1.0 |
>2.0 |
>2.0 |
>1.5 |
notes |
Cure condition: 25℃, RH70%, flame class UL94 V-0 |
Property |
Unit |
666 |
9391 |
9691 |
9695 |
9891 |
9893 |
Appearance |
|
Paste |
Paste |
Paste |
Paste |
Paste |
Paste |
Color |
|
White |
White |
Grey |
Grey |
Grey |
Grey |
Specific gravity |
g/cm3 |
2.1 |
2.3 |
2.6 |
2.7 |
2.8 |
2.8 |
Volatile |
At 120℃ |
<0.1% |
<0.14% |
<0.05% |
<0.05% |
<0.02% |
<0.02% |
Thermal resistance |
At 40psi |
<0.25 |
<0.25 |
<0.13 |
<0.09 |
<0.05 |
<0.04 |
Oil rate |
% |
<0.21 |
<0.20 |
<0.14 |
<0.15 |
<0.15 |
<0.12 |
Thermal conductivity |
W/m·k |
1.0 |
1.5 |
2.0 |
2.5 |
3.0 |
3.5 |
Working temperature |
℃ |
-50~200 |
-50~200 |
-50~200 |
-50~200 |
-50~200 |
-50~200 |
Property |
Unit |
L314 |
L316 |
L215 |
L217 |
L219 |
L153 |
Cure type |
|
Moisture |
Physic |
UV |
Physic |
Oxygen |
Moisture |
Similar product |
|
1-2577 |
1B51 |
|
1307 |
1301 |
3-1953 |
Appearance |
|
Light-yellow transparent |
Light-yellow transparent |
Transparent |
Transparent |
Purple transparent |
Transparent |
Viscosity |
mPa·s |
800 |
200 |
50 |
20 |
50 |
350 |
Cure time |
min |
20 |
12 |
1 |
6 |
6 |
10 |
Solid content |
% |
98 |
22 |
100 |
35 |
30 |
98 |
Volume resistance |
Ω.cm |
6 E+14 |
2E+14 |
5 E+14 |
2.6 E+14 |
2.1 E+14 |
3 E+15 |
Dielectric strength |
KV/mm |
21 |
18 |
28 |
28 |
26 |
20 |